17-09-2017, 09:20 AM #3i dont know if it would be any different for an is200 as for the mr2, but i used a mixture of autoglym metal polish and 3.5k grit micromesh, works a treat. As far as i know though, micromesh is quite tricky to get hold of, especially the really fine stuff.
17-09-2017, 09:25 AM
http://www.relishmodels.co.uk/alclad-ii-...h-set.html
Bit of info
http://www.ss-sci.com/micromesh.htm
if you go down that road, dont go too harsh, you will forever be polishing the fine scratches out. I had a go with 32k micromesh, its time consuming!!
OddScoobyMike
17-09-2017, 09:25 AM #4Saying that:
http://www.relishmodels.co.uk/alclad-ii-...h-set.html
Bit of info
http://www.ss-sci.com/micromesh.htm
if you go down that road, dont go too harsh, you will forever be polishing the fine scratches out. I had a go with 32k micromesh, its time consuming!!
17-09-2017, 09:50 AM
OddScoobyMike
17-09-2017, 09:50 AM #6wire wool isnt the best stuff to use on anything metal, you can cause an electrolytic reaction called dissimilar metal corrosion, its not ideal.
17-09-2017, 11:11 AM
OddScoobyMike wire wool isnt the best stuff to use on anything metal, you can cause an electrolytic reaction called dissimilar metal corrosion, its not ideal.
'Anything metal'?? Galvanic corrosion as you describe would only be a risk in this situation if you leave the stainless steel in contact with the carbon steel wire wool, or bits of it that may break off of it. Polishing the surface as you need to do after applying the Autosol removes any traces of carbon steel, and the risk of extended galvanic corrosion.
What's the risk of short term exposure? The difference in anodic index is probably less than 0.25V.
IS 200 Sport with a few mods, Standardish IS-F. The IS250 SE-L with a few mods has gone to a new home.[SIGPIC][/SIGPIC]
OddScoobyMike wire wool isnt the best stuff to use on anything metal, you can cause an electrolytic reaction called dissimilar metal corrosion, its not ideal.
'Anything metal'?? Galvanic corrosion as you describe would only be a risk in this situation if you leave the stainless steel in contact with the carbon steel wire wool, or bits of it that may break off of it. Polishing the surface as you need to do after applying the Autosol removes any traces of carbon steel, and the risk of extended galvanic corrosion.
What's the risk of short term exposure? The difference in anodic index is probably less than 0.25V.
IS 200 Sport with a few mods, Standardish IS-F. The IS250 SE-L with a few mods has gone to a new home.[SIGPIC][/SIGPIC]
18-09-2017, 01:41 AM
Tango I've always found fine grade wire wool and Autosol metal Polish works well
+1, great stuff
![[Image: sig.jpg]](http://www.aspo21.dsl.pipex.com//sig.jpg)
E55EX_RACER
18-09-2017, 01:41 AM #8Tango I've always found fine grade wire wool and Autosol metal Polish works well
+1, great stuff
18-09-2017, 02:45 AM
Tango 'Anything metal'?? Galvanic corrosion as you describe would only be a risk in this situation if you leave the stainless steel in contact with the carbon steel wire wool, or bits of it that may break off of it. Polishing the surface as you need to do after applying the Autosol removes any traces of carbon steel, and the risk of extended galvanic corrosion.
What's the risk of short term exposure? The difference in anodic index is probably less than 0.25V.
Thats why stainless steel exhausts rust, because of the electrolytic reaction.
Unless you do the whole thing, you cant guarantee getting all the bits from the wire wool off. personally, and its only my opinion, i wouldnt.
OddScoobyMike
18-09-2017, 02:45 AM #9Tango 'Anything metal'?? Galvanic corrosion as you describe would only be a risk in this situation if you leave the stainless steel in contact with the carbon steel wire wool, or bits of it that may break off of it. Polishing the surface as you need to do after applying the Autosol removes any traces of carbon steel, and the risk of extended galvanic corrosion.
What's the risk of short term exposure? The difference in anodic index is probably less than 0.25V.
Thats why stainless steel exhausts rust, because of the electrolytic reaction.
Unless you do the whole thing, you cant guarantee getting all the bits from the wire wool off. personally, and its only my opinion, i wouldnt.
Recently Browsing
1 Guest(s)
1 Guest(s)
Recently Browsing
1 Guest(s)
1 Guest(s)
Related Threads…
Replies 6
Views 918
Views 918
27-02-2019, 09:03 AM
Last Post byCyntax
Last Post by
Replies 1
Views 634
Views 634
16-11-2017, 09:18 AM
Last Post byRabster
Last Post by
Replies 1
Views 1,020
Views 1,020
05-05-2017, 09:32 PM
Last Post byLexusboy
Last Post by
Replies 0
Views 421
Views 421
11-05-2016, 09:46 PM
Last Post byLexusboy
Last Post by